Product mode
|
Application
|
Particle Size（AFS±3）
|
Heat bending strength（≥MPa）
|
Cold bending strength （≥Mpa）
|
Loss on ignition（≤%）
|
Sand properties
|
|
SD-1
|
Sand core, Cylinder block/head water jacket
|
52
|
3.5
|
8.5
|
3.0
|
1.High strength;
2.Low expansion, high temperature resistant.
|
|
SD-2
|
45
|
3.0
|
7.5
|
2.8
|
1.Low gas release, high gas permeability;
2.Low expansion, high temperature resistant.
|
|
SD-2N
|
Sand core, Cylinder block/head water jacket/hydraulic valve
|
60
|
4.0
|
9.0
|
4.0
|
1.High strength, high temperature resistant, low expansion;
2.Good stripping property, high resistance to sand burning.
|
|
SD-3
|
Sand core, Cylinder block/head water jacket
|
52
|
3.5
|
8.5
|
3.0
|
1.High resistance to heat shocks;
2.Good stripping property, high temperature resistant.
|
|
SD-SND-1
|
Sand core, Cylinder block/head water jacket
|
50
|
3.0
|
7.0
|
2.8
|
1. Low expansion, high temperature resistant;
2.Low gas release.
|
|
SD-SND-2
|
50
|
3.0
|
7.0
|
2.8
|
|
CFS75-GDD
|
Brake disc/camshaft
|
65
|
3.0
|
8.5
|
3.3
|
1.High strength, low gas release;
2.Low expansion, resistance to deformation.
|
|
CFS50-2N
|
Solid core
|
55
|
2.5
|
6.0
|
3.0
|
1.High temperature resistant;
2.High resistance to sand burning.
|
|
CFS50-3K
|
Shell mold(core)
|
55
|
3.5
|
7.5
|
3.4
|
1.Uniform shell, no shelling;
2.Rapid solidification.
|
|
CFS50-3KN
|
55
|
3.5
|
7.5
|
3.6
|
1.No shelling;
2.High resistance to sand burning.
|
|
CFS75-2TDF1
|
Solid core
|
65
|
3.0
|
7.0
|
2.1
|
1.High strength, low gas release;
2. Low expansio
|
|
CFS75-2DF2
|
Sand core, maniford
|
65
|
3.0
|
7.0
|
1.9
|
|
CFS75-5K
|
Shell core, transmission case
|
65
|
4.5
|
9.0
|
3.6
|
1.Good fluidity;
2.Perfect encrustation;
3.High strength;
4.Rapid solidification.
|
|
CFS50-5K
|
Shell core, large barrel
|
50
|
5.0
|
10.0
|
4.0
|
|
GK-5
|
Medium-size shell size
|
60
|
5.0
|
8.0
|
3.6
|
.jpg)